Designing of the Cooling Vest from Paraffin Compounds and Evaluation of its Impact Under Laboratory Hot Conditions

Saeid Yazdanirad, Habibollah Dehghan

Abstract


Background: The phase change materials (PCMs) have the appropriate properties for controlling heat strain. One of the well-known PCMs is paraffin. This study aimed to design the cooling vest from the cheap commercial paraffin compound and evaluation of its effectiveness under laboratory hot conditions.

Methods: the cooling vest was made of the polyester fabric and it had 17 aluminum packs. The each of aluminum packs was filled by 135 g of prepared paraffin with a proper melting point in the range of 15–35°C. an experimental study was conducted on ten male students under warm conditions (air temperature = 40°C, relative humidity = 40%) in a climatic chamber. Each participant was tested without cooling vest and with cooling in two activities rate on treadmill to include: light (2.8 km/h)
and moderate (4.8 km/h). The time of this test was 30 min in each stage. During the test, the heart rate, the oral temperature, the skin temperature were measured every 4 min. Finally, data were analyzed using the Kolmogrov–Smirnov and repeated measurement ANOVA test in SPSS 16.

Results: The latent heat of the prepared paraffin compound and the peak of the melting point were 108 kJ/kg and 30°C, respectively. The mean and standard deviation of heart rate, oral temperature, and skin temperature with cooling vest in light activity were 103.9 (12.12) beat/min, 36.77 (0.32)°C, and 31.01 (1.96)°C and in moderate activity were 109.5 (12.57) beat/min, 36.79 (0.20)°C, and 29.69 (2.23)°C, respectively. There is a significant difference between parameters with a cooling vest and without cooling (P < 0.05).

Conclusions: The designed cooling vest with low cost can be used to prevent thermal strain and to increase the physiological stability against the heat. However, the latent heat of this cooling vest was low.

Keywords: Cooling vest, heat strain, hot and dry conditions, paraffin